[0001] 1. Field of the Invention
[0002] The present invention relates to an oxide superconducting conductor allowing a large amount of superconducting critical current to pass therethrough incurring a small power loss, an oxide superconducting element wire for use in fabricating the conductor, and methods for fabricating the conductor and the element wire.
[0003] 2. Description of the Related Art
[0004] In a metallic superconducting conductor fabrication it has been widely practiced to fabricate a superconducting conductor by bundling superconducting element wires. When bundling the element wires, it is required to increase the critical current density of the element wire and to pass currents evenly through each of the element wires in order to attain a large current flow in a superconducting state, or a current flow incurring a small loss. To decrease the AC power loss in a metallic superconducting conductor, the use of a great number of fine element wires in a strand is practiced.
[0005] Further, in obtaining a superconducting element wire, efforts are being made to obtain a finer superconducting element wire having excellent flexibility and providing a greater critical current (Ic). In the case of a metallic superconducting element wire, a method to draw a bundle of coated wires is practiced.
[0006] In the oxide superconducting fabrication a similar method in practiced in metallic superconducting fabrication is also practiced in fabricating a Bi type oxide superconducting element wire, in which Bi type element wire has a Bi type superconducting core with a metallic sheath.
[0007] Recently, in fabricating a R
[0008] Such arts are described for example in Japanese Patent Laid-open No. Hei 1-93006, J. G. Wang et al., “Y—Ba—Cu—O superconducting fibers and wires by spray pyrolysis on carbon fibers”, J. Appl. Phys. Vol. 67 No. 4, pp. 2160-2162, or L. D. Woolf et al., “Continuous fabrication of high-temperature superconductor coated metal fiber and multifilamentary wire”, Appl. Phys. Lett. Vol. 58 No. 5, pp. 534-536.
[0009] Crystals of oxide superconductors generally have the orthorhombic crystal structure. The orthogonal axes of the orthorhombic lattice are called a-axis, b-axis, and c-axis in ascending order of the lengths of the axes. Of these axes, since the a-axis and b-axis have nearly the same length, they are frequently not discriminated from each other and are called the a-axis or the ab-axis. Since the superconducting current flows in the CuO plane perpendicular to the c-axis, a great superconducting current flow takes place in the direction perpendicular to the c-axis. On the other hand, the superconducting critical current density (Jc) is low in the direction parallel to the c-axis. Accordingly, in an oxide superconducting element wire aimed at obtaining a large current flow, it becomes necessary to arrange the c-axis of the crystal perpendicular to the direction of the current flow.
[0010] In a tape-formed or plate-formed substrate, a thin film whose c-axis is oriented in the perpendicular direction to the surface of a base material (such a film may hereinafter be called a c-axis oriented film) was formed by suitably selecting the forming conditions, such as depositing temperature and the like, for depositing the oxide superconducting thin film.
[0011] Another factor impeding the flow of a superconducting current, especially in the c-axis oriented film is a grain boundary caused by the crystals having different orientations in the a- and b-axes. This tendency is particularly remarkable in the case of a R
[0012] A method tried first to form an intermediate layer having a crystal alignment by an ion beam assist deposition method or an inclined substrate method (ISD method) and then to form a superconducting thin film with an crystal alignment on the intermediate layer by a pulse laser deposition method (PLD method) or a metal organic chemical vapor deposition method (MOCVD method) on a plate formed substrate for reducing the number of the grain boundary. Another method was tried which uses a thin film formed on a long and narrow single crystalline base material by such a method as a liquid phase epitaxial method, so that a crystal orientation is provided for the oxide superconducting thin film.
[0013] As to the ion beam assist deposition method, reference is made to the disclosure, for example, in Y. Iijima et al., “In-plane aligned YBa
[0014] (1) Of the above mentioned related art examples, that using a fiber as the core was not succeeded to align the crystal orientation of the superconducting layer and, hence, there were problems such that (a) the critical current density was restricted to a low value. And if applying the thick superconducting layer for passing enough electric current, then (b) the mechanical characteristics such as flexibility tend to deteriorate because of the superconducting layer thickness.
[0015] These problems are described in detail below.
[0016] (a) In order to form an oxide superconducting thin film with excellent superconducting characteristics it is required to align the crystal orientation of the oxide superconducting thin film. To align the said orientation, it is required either to irradiate the substrate with an ion beam directed thereto at a specific angle or to deposit a material on the substrate in a specific angular direction.
[0017] However, with a fine and round base material such as a fiber, it was thought to be impossible to make constant the irradiating angle of the ion beam or the deposited angle of the material with respect to the surface of the base material, and therefore it was thought to be impossible to obtain an oxide superconducting thin film with good crystal alignment. Hence, the critical current density was restricted to a low value. One example of the attempt was reported to provide a thin superconducting layer by a pulse laser deposition method with a carbon fiber as a core (A. Al-Sharif et al., “Attempts to prepare Bi-based superconductor on a carbon fiber substrate”, J. Appl. Phys. Vol. 67 No. 9, pp. 5023-5025).
[0018] (b) As to the thickness of the superconducting layer, a superconducting current is known that flows only very near the surface of the superconductor. The pertinent thickness is considered to be around 1 μm, against which, the superconducting layer in the above described related art example was as thick as several tens of μ m.
[0019] The thick superconducting layer has no contribution to the current flow amounts, and further, by the strain produced by bending at the circumferential portion of the layer, where the current flow is large, and results in deterioration of the superconducting characteristic of the wire element.
[0020] (2) As to the shape of an element wire in a tape form or plate form, the conductor design is greatly restricted and it is difficult to calculate the inductance accurately. This is described in detail below.
[0021] A tape-formed and a plate-formed element wire having a high Jc value obtained in the above-described related art, however, the direction to be bent is restricted and prevents processing in the desired conductor shape. Especially when the obtained superconducting element wires are stranded for making conductor, the manner of the stranding is greatly restricted. For example, when the wires are twisted together, the pitch in the strand must be made somewhat larger. This also causes difficulty when the superconducting conductors must be bent in actual use.
[0022] And as the tape-formed or plate-formed superconducting wire has a considerable width, the current flow pass is difficult to estimate. Therefore, when element wires are twisted together or stranded in a spiral form, it is impossible to design the inductance accurately.
[0023] Accordingly, an object of the present invention is to provide an oxide superconducting element wire, as well as an oxide superconducting conductor formed by bundling the element wires, allowing a large amount of superconducting current to flow therethrough, providing a large degree of freedom in the form of the combination of the element wires, and providing ease in the design of the inductance more accurately, and to provide a method of fabricating the same.
[0024] Another object of the present invention is to provide a method of fabrication of an oxide superconducting element wire, as well as an oxide superconducting conductor formed by bundling the element wires, capable of forming a superconducting film virtually uniform in thickness through a single film forming process with the use of a simple film forming apparatus or plural forming equipment, even if a base material of a circular cross-section is used.
[0025] The inventors found some samples which exhibited a superior superconducting critical current density (Jc), when forming an oxide superconducting thin film on an intermediate layer formed on a base material of a circular cross-section by a pulse laser deposition method.
[0026] This is considered to be due to the fact that the same angle as obtained in the inclined substrate deposition method is formed between the deposited particles and the surface of the base material at a portion of the outside surface of the circular cross section, resulting in the formation of the aligned crystal orientation at the portion of the intermediate layer on the base material, and then the aligned oxide superconducting thin film is formed on the intermediate layer. Further, it has been found that an aligned oxide superconducting thin film having in a continuous longitudinal direction of the base material can be formed by continuously forming in the longitudinal direction with moving forward the base material having the aligned intermediate layer.
[0027] The inventors analyzed the above result deeply with the pre-described references.
[0028] An intermediate layer of YSZ (Yttrium Stabilized Zirconium Oxide) or CeO
[0029] Therefore, the oxide superconducting element wire of the invention, in an oxide superconducting element wire obtained by forming an oxide superconducting thin film on the surface of a long and flexible base material, has a circular, elliptical, or regular polygonal cross-section orthogonal to the longitudinal direction of the base material, the oxide superconducting thin film has a portion in which a crystal orientation is three-axes aligned, and the portion having the three-axes aligned crystal orientation is continuously arranged in the longitudinal direction.
[0030] The oxide superconducting thin film on the surface of the oxide superconducting element wire of the invention is not completely three-axes aligned on the whole of the wire surface. Therefore, if seen only from the viewpoint of the value Jc of the oxide superconductor, that using a tape-formed base material in the related art can provide a higher Jc value. However, an oxide superconducting conductor obtained by bundling the element wires of the invention has a larger sectional area of the oxide superconductor than that obtained by bundling the tape-formed element wires, and hence it can pass a larger superconducting current flow.
[0031] Table 1 shows examples of trial calculations of Ic and others for the cases where a superconducting conductor 1 cm square is provided by 100 pieces in lamination of tape-formed superconducting element wires, each being of 10 mm wide×0.1 mm thick, and by bundling fine element wires of circular cross-sections.
TABLE 1 Trial Calculation for Fabrication of Superconducting Conductor Supercond Number Supercond ucting of Form of Element ucting Thin Film Assumed Element Element Wire Thin Film Sectional Jcx Wires Wire Size Thickness Area (cm (A/cm (Pieces) IC(A) Tape 0.1 × 1 μm 1.00 × 10 2.0 × 10 100 2,000 Form 1 mm Circular 0.01 mm 1 μm 2.83 × 10 8.0 × 10 1,000,000 2,262 Cross- Φ section 0.05 mm 1 μm 1.54 × 10 4.0 × 10 40,000 2,463 Φ 0.1 mm 1 μm 3.11 × 10 6.6 × 10 10,000 5,053 Φ
[0032] As apparent from Table 1, when thin wires of a circular cross-section are used, the value Jc of the superconducting thin film providing the same level of Ic can be made considerably smaller than when tape-formed element wires are used. While Table 1 shows the results of trial calculation in the case where superconducting element wires are simply bundled, it is necessary to strand the element wires in a spiral form or the like in the case of AC power transmitting superconducting conductors to decrease penetration of the current into the interior and increase loss of power. When such processing must be done, fine and circular element wires excellent in workability can greatly reduce the diameter of the cross-section of the superconducting conductor.
[0033] Further, since fine element wires of a circular cross-section have better workability than tape-formed element wires, they allow free designing of the form of bundling. This provides merits such that a thinner superconducting conductor can be produced for a required current value, a flat superconducting conductor can be produced depending on the conditions of the installed position, and the element wires can be stranded such that they are transposed from each other to thereby pass AC current incurring a small loss. Further, with the fine element wires of a circular cross-section, accurate calculation of the inductance can be made more easily than with the tape-formed element wires.
[0034] In order to increase the area, in which the crystal orientation is three-axes aligned, it is also effective to use a regular polygonal cross-section wire. By keeping the depositing angle of the material or the radiating direction of the ion beam with respect to each surface of the polygon constant, the crystal orientation in the intermediate layer can be in-plane aligned and, consequently, a three-axes alignment in the oxide superconducting thin film on each surface of the base material can be obtained.
[0035] In reality, when a fine base material of a regular polygonal cross-section is used, it may be difficult to keep a specific surface of the base material in a fixed angle to the deposited direction of the material through separate processing. However, if the material deposition is performed in succession to the process of forming the base material into a regular polygonal cross-section, it becomes easier to keep the surface of the base material in constant angular relationship with the material deposited direction. Further, if the forming portion is heated to keep at a most suitable temperature at the deposited portion, an oxide superconducting element wire providing excellent performance can be fabricated by simpler or succession processing.
[0036] In the oxide superconducting element wire as described above, the portion in which a crystal orientation is three-axes aligned is, preferably, extended continuously from around one end to around the other end of the oxide superconducting element wire.
[0037] Thereby, it becomes possible to flow a greater amount of superconducting current from around the one end to around the other end.
[0038] The method to achieve the above described oxide superconducting element wire is to provide an intermediate layer between the oxide superconducting thin film and the base material, to form in the intermediate layer a portion in which a crystal orientation is in-plane aligned and extended continuously in the longitudinal direction, and to form on the surface thereof the oxide superconducting thin film, so that the crystal orientation in the oxide superconducting thin film is extended continuously in the longitudinal direction in accordance with the crystal orientation in the intermediate layer.
[0039] Thereby, it is possible to obtain, even on the surface of an element wire of a circular cross-section, an oxide superconducting thin film having a portion in which a crystal orientation is three-axes aligned.
[0040] In the above described oxide superconducting element wire, the base material is, preferably, a metallic wire or a ceramic wire.
[0041] Thus, it becomes possible to select suitable material of the base material.
[0042] In the oxide superconducting element wire, the thickness of the oxide superconducting thin film is, preferably, sufficiently small so as to allow the transmitted electromagnetic energy to penetrate into the oxide superconducting thin film.
[0043] Thereby, the portion of the superconducting thin film not contributing to the superconducting current flow can be made smaller. Therefore, this not only improves the efficiency but the strain caused by bending at the peripheral portion where the current flows can also be decreased to improve the superconducting characteristics.
[0044] In the above described oxide superconducting element wire, the thickness of the oxide superconducting thin film is, preferably, 1.2 μm or less.
[0045] While the length of penetration of the magnetic field in a typical oxide superconductor is said to be a little larger than 1 μm, at the longest, if the film thickness is 1.2 μm or more, a favorable energy transmission efficiency for each unit volume of the conductor can be obtained. However, if there exists a deteriorated layer in the interface of the oxide superconducting thin film and the base material, the thickness of the deteriorated layer must be compensated for and, further, the thickness of the thin film must sometimes be made slightly larger to provide a good superconducting thin film. Therefore, the aforesaid thickness of the oxide superconducting thin film is not essentially limiting the present invention.
[0046] In the above-described oxide superconducting element wire, there is, preferably, further provided a metallic thin film covering the periphery of the oxide superconducting thin film.
[0047] In the above-described oxide superconducting element wire, there is, preferably, further provided an insulating thin film covering the periphery of the oxide superconducting thin film. In the above described oxide superconducting element wire, the oxide superconducting thin film, preferably, has a composition of R
[0048] In the above-described superconducting element wire, the material of the intermediate layer is preferably selected from YSZ and CeO
[0049] In the above described oxide superconducting element wire, the maximum length of straight lines connecting any two points on the sides of the cross-section perpendicular to the longitudinal direction (including the diameter) of the element wire is, preferably, 1 mm or less.
[0050] As to the diameter of the superconducting element wire, if it is too large, no current flows through the superconducting element wires in the interior because the electromagnetic field is shielded by the superconducting element wires in the circumferential portion. Also, flexibility of the superconducting element wire deteriorates when the diameter is too large. In view of these points, it is preferred that the size of the element wire for use in commercial frequency from 50 Hz to 60 Hz be 1 mm or less. As to the values of the frequency, they are simply mentioned as typical examples in use today. The aforesaid effects are essentially unchanged even if the values are changed to a certain degree.
[0051] In the above described oxide superconducting element wire, the base material is, preferably, made of a material having a larger coefficient of thermal expansion than the oxide superconducting thin film.
[0052] This is because characteristics of the oxide superconducting thin film normally suffers greater tensile strain than compressive strain. Hence, it is desired that the thin film formed in a high temperature condition and then cooled down to normal temperature should not be subjected to a tensile stress.
[0053] The oxide superconducting conductor of the invention is such that is obtained by combining a plurality of any of the above described oxide superconducting element wires. (In this specification “stranding” hereinafter may mean the processing of bundling, simply gathering or collecting, twisting and bunching a plurality of oxide superconducting element wires together for processing a plurality of superconducting element wires in the longitudinal direction to make an oxide superconducting conductor. In said stranded conductor each of the wires changes its radial position from the outer to inner and from the inner to outer sides of the oxide superconducting conductor, i.e., such that they are transposed with each other.)
[0054] It is therefore possible to obtain an oxide superconducting conductor that allows a flow of a large amount of superconducting current, provides a high degree of freedom in the design of the form of combination of the wires, and allows easy designing of the inductance.
[0055] In the above described oxide superconducting conductor, the plurality of oxide superconducting element wires are stranded, preferably, twisted together, in the longitudinal direction such that each of the oxide superconducting element wires changes its radial position from the outer to inner and from the inner to outer sides in the length direction of the oxide superconducting conductor (i.e., such that they are transposed).
[0056] Thus, by having a plurality of oxide superconducting element wires twisted together or transposed, an oxide superconducting conductor can be obtained.
[0057] A method of fabricating an oxide superconducting element wire according to an aspect of the invention comprises the following steps:
[0058] First, a long and flexible base material of a circular, elliptical, or regular polygonal cross-section orthogonal to the longitudinal direction is prepared. Then, an intermediate layer of a structure in which a portion with a crystal orientation in-plane aligned is extended continuously in the longitudinal direction is formed on the surface of the base material. Then, an oxide superconducting thin film is formed on the surface of the intermediate layer.
[0059] In the method of fabricating an oxide superconducting element wire according to an aspect of the invention, an oxide superconducting thin film is formed on an intermediate layer having a portion in which a crystal orientation is in-plane aligned as described above, which makes it possible to form an oxide superconducting thin film having a portion in which a crystal orientation is three-axes aligned. It is therefore, possible to obtain an oxide superconducting element wire constituting an oxide superconducting conductor that allows a large flow of superconducting current, providing a high degree of freedom in the design of the form of combination, and allowing easy designing of the inductance.
[0060] In the method of fabricating an oxide superconducting element wire in the aforesaid aspect, an intermediate layer is, preferably, formed in succession to a step in which the base material made of a metallic wire is heated while being formed to have a regular polygonal cross-section orthogonal to the longitudinal direction. In the formation of the intermediate layer, the material of the intermediate layer is deposited to have a predetermined angular direction with respect to a specific surface of the base material or the material of the intermediate layer is deposited while an ion beam is radiated at a predetermined angular direction to a predetermined surface of the base material so that a portion of the intermediate layer on the specific surface of the base material is provided with an in-plane alignment.
[0061] It is, therefore, possible to provide the intermediate layer with a portion in which a crystal orientation is in-plane aligned.
[0062] In the method of fabricating an oxide superconducting element wire in the above described aspect, the oxide superconducting thin film is, preferably, formed by one or more methods selected from the group of pulse laser deposition method, sputtering method, chemical vapor deposition method, liquid phase epitaxial method, and MOCVD method.
[0063] It is, therefore, possible to select a suitable method of fabricating the oxide superconducting thin film.
[0064] In the method of fabricating an oxide superconducting element wire in the above described aspect, there is, preferably, further provided the step of forming at least one of a metallic thin film and an insulating thin film for covering the periphery of the oxide superconducting thin film. The step of forming at least either of the metallic thin film and the insulating thin film is performed in succession to the step of forming the intermediate layer and the oxide superconducting thin film.
[0065] This prevents the surface of the intermediate layer from deterioration in between the processes of forming the intermediate layer and the oxide superconducting thin film. Hence, not only the productivity is improved but also the superconducting characteristics.
[0066] According to a method of fabricating on oxide superconducting conductor in an aspect of the invention, an oxide superconducting conductor is formed by combining the oxide superconducting element wires obtained in the method of fabrication with any of the above described aspects.
[0067] Thus, an oxide superconducting conductor that allows a large flow of superconducting current, provides a high degree of freedom in the form of combination, and allows easy designing of the inductance can be obtained.
[0068] In the method of fabricating an oxide superconducting conductor in the above described aspect, the step of forming the oxide superconducting conductor by combining the oxide superconducting element wires is, preferably, performed in succession to the step of fabricating the oxide superconducting thin film or the step of forming at least either of the metallic thin film and the insulating thin film.
[0069] Therefore, the oxide superconducting element wires need not be taken up on reels but can be successively stranded directly into an oxide superconducting conductor. Thus, the oxide superconducting conductors can be fabricated more efficiently. Of course, several pieces of the conductors can further be stranded to produce an oxide superconducting conductor allowing a greater critical current to pass therethrough. Further, since a plurality of element wires can be fabricated at the same time, the productivity is further improved.
[0070] In the physical deposition method such as the PLD method, the direction in which the thin film is deposited is limited by the flying direction of the material of the thin film. Therefore, when a thin film is deposited on a thin and round base material such as a fiber by a physical deposition method such as the PLD method, the superconducting layer is not formed on one half of the cross-section of the base material. Hence, in order to cover the entire surface of the base material with the superconducting layer, the thin film forming process must be performed two times or the targets must be disposed in two places. If it is further considered to make the thickness uniform, it is necessary to repeat the film forming process additional times or to dispose targets in additional places.
[0071] Further, when there are a number of dents present on the surface of the base material, the frequency of repetitions of the film forming process or the number of disposed targets must be increased further to uniformly form the superconducting thin film also in such dents.
[0072] The same is applicable to the case of forming of an intermediate layer between the base material and the superconducting layer. The intermediate layer is especially required for preventing the superconductivity from deterioration by the diffusion of the base material into the superconducting layer. Therefore, when the intermediate layer fails to cover the entire surface of the base material, the superconducting layer may be completely deteriorated by the diffusion from the portion not recovered by in the intermediate layer and, in the worst case, possibly no superconducting current will flow.
[0073] The inventors found that an oxide superconducting thin film with uniform thickness can be formed by using a simple film forming apparatus and in only one film forming step by using a method such as a metal organic chemical deposition (MOCVD) method as the thin film forming means to form an oxide superconducting thin film on the surface of a base material of a circular cross section or another cross section, instead of the above described pulse laser deposition method or the like, in which directivity in the deposition on the base material is high.
[0074] Uniform thickness, here, is defined as a thickness of which variation is within ±10%.
[0075] Since this method of fabrication, as a means of thin film formation, is performed with less directivity in the deposition on the base material than that of the above described pulse laser deposition method or the like, a thin film can be formed uniform thickness on the entire periphery of the base material.
[0076] In the formation of the intermediate layer, however, it is difficult to control the crystal orientation by this method. One effective solution is to use the method to irradiate ion beams at a specific angle during the film formation. The film formation and ion beam irradiation is carried out by alternately repeating the film formation and the ion beam irradiation in forming an intermediate layers having a portion of an in-plane alignment. Then, by forming thereon an oxide superconducting layer by the MOCVD method, a portion in which three-axes alignment is established could be obtained in the superconducting layer.
[0077] Although the Jc value of the oxide superconductor itself is also lower than that of the tape-formed base material, it can pass a larger amount of superconducting current therethrough than that of the tape-formed base material as shown in Table 1, when superconducting element wires obtained by this method are stranded into a superconducting conductor.
[0078] As to the material and structure of the oxide superconducting element wire produced by this method and the method of fabricating the oxide superconducting conductor by combining the element wires, it should be noted here that the same material, structure, and fabricating method as described above are used.
[0079] It should further be noted here that the continuous performance of the steps to form the required layers (intermediate layer, superconducting thin film, and protecting layer) is advantageous from the viewpoint of not only the productivity but also product performances. For example, the problems of surface deterioration produced during the time between the formation of the intermediate layer and the superconducting thin film or between the formation of the superconducting thin film and the protecting layer, in the lower layer can be obviated by forming these layers in succession.
[0080] Further, since the diameter of the element wire of the circular-cross section can be made smaller than that of the tape-formed element wire, a plurality of element wires can be simultaneously processed with a film forming apparatus. Therefore, in producing superconducting element wires described herein, it is more efficient to fabricate a plurality of element wires at the same time.
[0081] Further, the simultaneous fabrication of all the required element wires for making a superconducting conductor makes it possible to continuously strand the element wires without taking up the element wires and, thereby, the superconducting conductor can be fabricated more efficiently. Of course, it is possible to further strand a plurality of the thus stranded wires to thereby obtain a superconducting conductor allowing a larger flow of critical current.
[0082] Further, the intermediate layer and the protecting layer of uniform thickness can be formed by the use of a simple film forming apparatus in a single film-forming step, and thereby the superconducting thin film is prevented from deteriorating in its entirety by diffusion.
[0083]
[0084]
[0085]
[0086]
[0087]
[0088] Embodiments of the invention will be described with reference to the accompanying drawings.
[0089]
[0090] Referring to
[0091] The oxide superconducting layer
[0092]
[0093] In more concrete terms, two element wires
[0094] As the base material
[0095] The oxide superconducting thin film
[0096] It is preferred that the diameter of the oxide superconducting element wire
[0097] Further, it is preferred that the base material
[0098] Further, it is preferred that the diameter of the element wire
[0099] A method of fabricating a superconducting conductor in an embodiment of the invention will be described below.
[0100]
[0101] Each of the forming chambers in the thin film-forming vessel is separated by partition walls
[0102] The intermediate layer and the oxide superconducting thin film are formed by a PLD method, and the protective layer is formed by a RF sputtering method. The wires
[0103]
[0104] A case where a plurality of element wires
[0105] While cases where oxide superconducting thin films
[0106] The intermediate layer
[0107]
[0108] The flanges
[0109] The base material
[0110] Then, in the superconducting film-forming chamber
[0111] Then, in the protective film-forming chamber
[0112] Superconducting element wires are fabricated as described above and they are stranded and taken up in the stranding and taking-up portion
[0113]
[0114] While a case where the protective layer is formed by the DC sputtering method has been described above, it may be formed by the MOCVD method or another method. Further, though a case where the intermediate layer is formed by the MOCVD method has been described above, it may otherwise be formed by a method such as the sputtering method. While a case where the oxide superconducting thin film is formed for example by the MOCVD method has been described above, it may be formed by any another method which like the MOCVD method makes it possible to form an oxide superconducting thin film of uniform thickness around the circumference of the base material through a single thin film forming step.
[0115] Examples of the present embodiment will be described below.
[0116] First, in the apparatus configured as shown in TABLE 2 Thin Film Forming Thickness Layer Method Temperature Atmosphere (μm) YSZ PLD 500° C. 50 mTorr (Ar) 0.8 YBCO PLD 770° C. 100 mTorr (O 0.8 Silver DC Room Sputtering Temperature 0.1 mTorr 2.0 YSZ RF Room Sputtering Temperature 50 mTorr (Ar) 0.8
[0117] The formation of the layers
[0118] Twenty pieces of the element wires fabricated as described above have been stranded to fabricate an oxide superconducting conductor. The average value of Ic of the element wires at 77 K was 5.6 mA and the value of Ic of the conductor obtained by combining the same was 108 mA. This value proves to be higher than the value of Ic of an oxide superconducting conductor fabricated by combining element wires in a tape form. The critical current density of the YBCO layer (oxide superconducting thin film) is estimated at around 4× 10
[0119] Referring to
[0120] Twenty pieces of the element wires fabricated as described above were stranded to provide an oxide superconducting conductor. The average value of Ic of the element wires at 77 K was 4 mA and the value of Ic of the conductor obtained by bundling the same was 77 mA. This value is that of a product experimentally produced by a laboratory scale apparatus. If they are produced by a dedicated apparatus under suitably controlled conditions, characteristics of the product and the number of superconducting element wires to be stranded will be increased.
[0121] The embodiments and examples disclosed herein, in all of their aspects, are solely illustrative and not limitative of the invention. The scope of the invention is determined not by the foregoing description but by the accompanying claims and various changes and modifications that fall within the equivalent spirit and scope of the claims that are intended to be embraced by the claims.
[0122] According to the present invention, as described in the foregoing, since a superconducting conductor is fabricated by combining superconducting element wires superior in workability, the degree of freedom in the design of the superconducting conductor, namely, the manner of combining the element wires, can be enhanced. It is, therefore, possible to obtain superconducting conductors suitable for each of the applications and to allow a large amount of superconducting current to flow therethrough.