US20150240338 Ultra-Thick High Strength 7xxx Series Aluminum Alloy Products and Methods of Making Such Products  
The present invention is directed to an ultra-thick high strength aluminum alloy, comprising 7.5 to 8.4 wt. % Zn, 1.6 to 2.3 wt. % Mg, 1.4 to 2.1 wt. % Cu, and 0.05 to 0.15 wt. % Zr. This alloy...
US20140246127 HIGH-STRENGTH ALUMINUM ALLOY AND PROCESS FOR PRODUCING SAME  
A high-strength aluminum alloy material having a chemical composition which includes Zn: more than 7.2% (mass %, the same applies hereafter) and 8.7% or less, Mg: 1.3% or more and 2.1% or less,...
US20050211350 In-line method of making T or O temper aluminum alloy sheets  
A method of making aluminum alloy sheet in a continuous in-line process is provided. A continuously-cast aluminum alloy strip is optionally quenched, hot or warm rolled, annealed or heat-treated...
US20050087267 Aluminum alloy product and method of manufacturing the same  
An aluminum alloy product includes additive elements of 3.0 to 4.2 wt % of silicon, 0.4 to 0.6 wt % of magnesium, 0.2 wt % or less of iron, and 0.5 wt % or less in total of zinc, manganese,...
US20050039831 Blister-free aluminum forgings and method of making the same  
An aluminum alloy, which is more resistant to high temperature oxidation-type blistering, comprises: about 0.65-0.9 wt. % silicon, about 4-4.6 wt. % copper, about 0.6-0.9 wt. % manganese, about...
US20120227873 METHOD FOR TEMPERING AN ALUMINUM ALLOY  
A process for tempering large aluminum lithium alloy component parts to achieve high strength capability and resistance to stress corrosion cracking without the need for the prior art step of cold...
US20140124103 HIGH-STRENGTH ALUMINUM ALLOY MATERIAL AND PROCESS FOR PRODUCING THE SAME  
A high-strength aluminum material having a chemical composition which includes Zn: more than 7.2% (mass %, the same applies hereafter) and 8.7% or less, Mg: 1.3% or more and 2.1% or less, Cu: less...
US20100028101 Hot pressing process, particularly for providing metal unions for pneumatic, hydraulic and fluid-operated circuits, and metal union obtained thereby  
A hot pressing process, particularly for providing metal unions couplings for pneumatic, hydraulic and fluid-operated circuits, and a resulting metal union. The hot pressing process comprising: a...
US20110017055 5XXX ALUMINUM ALLOYS AND WROUGHT ALUMINUM ALLOY PRODUCTS MADE THEREFROM  
Improved 5xxx aluminum alloys and products made therefrom are disclosed. The new 5xxx aluminum alloy products may achieve an improved combination of properties due to, for example, the presence of...
US20080257462 ALUMINUM ALLOY MATERIAL FOR HIGH-TEMPERATURE/HIGH-SPEED MOLDING, METHOD OF PRODUCING THE SAME, AND METHOD OF PRODUCING A MOLDED ARTICLE OF AN ALUMINUM ALLOY  
An aluminum alloy material for high-temperature/high-speed molding containing 2.0 to 8.0 mass % of Mg, 0.05 to 1.0 mass % of Mn, 0.01 to 0.3 mass % of Zr, 0.06 to 0.4 mass % of Si and 0.06 to 0.4...
US20060151075 Low internal stress Al-Zn-Cu-Mg plates  
The present invention relates to a method for producing Al—Zn—Cu—Mg type alloy plates comprising between 4 and 12% zinc, less than 4% magnesium and less than 4% copper, other elements≦0.5% each,...
US20070169861 Material on the basis of an aluminum alloy, method for its production, as well as use therefor  
The invention concerns a method for producing a substance during which an aluminum base alloy is produced that has a content of 5.5 to 13.0% by mass of silicon and a content of magnesium according...
US20080236708 Process For Manufacturing Structural Components By Machining Plates  
The present invention includes a process for manufacturing metal sheets or plates and a machined metal part as well as machined products, structural components and their uses in various...
US20100243113 THERMOMECHANICAL PROCESSING OF ALUMINUM ALLOYS  
A cast aluminum alloy containing up to about 0.35% by weight chromium is heated to a first elevated temperature to homogenize the casting and dissolve the chromium content in an aluminum-based...
US20170101705 OPTIMIZATION OF ALUMINUM HOT WORKING  
A method of hot forming an aluminum alloy component may include heating the aluminum alloy component in a heating furnace to a solutionizing temperature, cooling the aluminum alloy component to a...
US20170081748 A METHOD OF FORMING PARTS FROM SHEET METAL ALLOY  
A method of forming a part from sheet metal alloy is provided, for example, forming a part from aluminium alloy. The method comprises heating (A) the sheet metal alloy to a temperature at which...
US20150376727 METHOD FOR THE MANUFACTURING OF ELEMENTS OF NON-FERROUS METAL ALLOYS, ADVANTAGEOUSLY ALUMINIUM ALLOYS  
A method is disclosed for the manufacturing of elements of non-ferrous metal alloys, advantageously aluminium alloys, used for the manufacturing of shaped elements, in particular rods, in thermal...