US20140137995 ALUMINUM-COPPER ALLOYS CONTAINING VANADIUM  
New 2xxx aluminum alloys containing vanadium are disclosed. In one embodiment, the aluminum alloy includes 3.3-4.1 wt. % Cu, 0.7-1.3 wt. % Mg, 0.01-0.16 wt. % V, 0.05-0.6 wt. % Mn, 0.01 to 0.4 wt....
US20080240976 EXTRUSION PRODUCT MADE OF ALUMINUM/ALUMINUM ALLOY MATRIX COMPOSITE AND A PROCESS OF FORMING THE EXTRUSION PRODUCT  
A process of an extrusion product made of matrix composite aluminum alloys has multiple steps. First, provide at least two different aluminum alloys. Select one of the aluminum alloys to be a...
US20090053098 7000-SERIES ALUMINUM ALLOY EXTRUDED PRODUCT AND METHOD OF PRODUCING THE SAME  
An extruded product includes a 7000-series aluminum alloy, the 7000-series aluminum alloy having an excess Mg content or an excess Zn content of less than 0.5 mass % with respect to a...
US20130146188 METHOD OF MANUFACTURING ALUMINUM-CONTAINING COMPOSITION AND PRODUCT MADE FROM SUCH COMPOSITION  
The present invention is concerned with a method of manufacturing an aluminum-containing composition, wherein the composition having substantially 0.4 wt % silicon, 0.7 wt % iron, 0.2 wt % copper,...
US20150167137 ALUMINUM ALLOY FOR MICROPOROUS HOLLOW MATERIAL WHICH HAS EXCELLENT EXTRUDABILITY AND GRAIN BOUNDARY CORROSION RESISTANCE, AND METHOD FOR PRODUCING SAME  
An aluminum alloy for microporous hollow shape material use constituted by an aluminum alloy which has excellent corrosion resistance and extrudability which keeps down the content of Cu which...
US20070128463 MULTI-ALLOY MONOLITHIC EXTRUDED STRUCTURAL MEMBER AND METHOD OF PRODUCING THEREOF  
The present invention provides a structural member of a multi-alloy monolithic extrusion comprising a first aluminum alloy and a second aluminum alloy; wherein the first aluminum alloy is...
US20050189047 Aluminum alloy extruded product for heat exchangers and method of manufacturing the same  
A high-strength aluminum alloy extruded product for heat exchangers which excels in extrudability, allows a thin flat multi-cavity tube to be extruded at a high critical extrusion rate, and excel...
US20110155291 High-strength aluminum alloy extruded product exhibiting excellent corrosion resistance and method of manufacturing same  
The present invention provides a high-strength aluminum alloy extruded product exhibiting excellent corrosion resistance and secondary workability and suitably used as a structural material for...
US20080277036 METHOD FOR MANUFACTURING TANKS  
The invention relates to the manufacture of tanks from one ore more metal plates using a friction stir welding process The metal plate or plates is first formed into a tubular shape with one pair...
US20110017359 HIGH STRENGTH L12 ALUMINUM ALLOYS  
High strength heat treatable aluminum alloys that can be used at temperatures from about −420° F. (−251° C.) up to about 650° F. (343° C.) are described. The alloys are strengthened by dispersion...
US20100051147 High-strength aluminum alloy extruded product exhibiting excellent corrosion resistance and method of manufacturing same  
The present invention provides a high-strength aluminum alloy extruded product exhibiting excellent corrosion resistance and secondary workability and suitably used as a structural material for...
US20130319585 Aluminum Alloy Combining High Strength, Elongation and Extrudability  
An aluminum alloy includes, in weight percent, 0.70-0.85 Si, 0.14-0.25 Fe, 0.25-0.35 Cu, 0.05 max Mn, 0.75-0.90 Mg, 0.12-0.18 Cr, 0.05 max Zn, and 0.04 max Ti, the balance being aluminum and...
US20120145365 ALUMINUM ALLOY HEAT EXCHANGER AND METHOD OF PRODUCING REFRIGERANT TUBE USED FOR THE HEAT EXCHANGER  
An aluminum alloy heat exchanger is produced by applying a coating material that is prepared by adding a binder to a mixture of an Si powder and a Zn-containing compound flux powder to a surface...
US20150167130 Composite Pistons for Rotary Engines  
A light metal material having a tensile strength of >180 MPa at room temperature is provided, as well as a method for producing such a light metal material and the use of such a light metal...
US20160194742 ALUMINUM ALLOY WIRE ROD, ALUMINUM ALLOY STRANDED WIRE, COATED WIRE, WIRE HARNESS AND MANUFACTURING METHOD OF ALUMINUM ALLOY WIRE ROD  
An aluminum alloy wire rod has a composition consisting of 0.1-1.0 mass % Mg; 0.1-1.0 mass % Si; 0.01-1.40 mass % Fe; 0.000-0.100 mass % Ti; 0.000-0.030 mass % B; 0.00-1.00 mass % Cu; 0.00-0.50...
US20160153073 ALUMINUM ALLOY HAVING AN EXCELLENT COMBINATION OF STRENGTH, EXTRUDABILITY AND CORROSION RESISTANCE  
An aluminum alloy having an excellent combination of strength, extrudability and corrosion resistance may include in weight percent, about 0.01% or less copper; about 0.15% or less iron; about...
US20150354045 7XXX Series Alloy with Cu Having High Yield Strength and Improved Extrudability  
7000 series aluminum alloys containing copper are provided. The aluminum alloys have high yield strength, and in some aspects allow press quenchability and/or have extrusion speeds more rapid than...
US20150303165 ALUMINUM ALLOY WIRE FOR BONDING APPLICATIONS  
The invention is related to a bonding wire containing a core having a surface. The core contains aluminum as a main component and scandium in an amount between 0.05% and 1.0%.