DETAILED DESCRIPTION OF THE INVENTION

[0035] The process of the invention, typically carried out in a fixed bed reactor system or a recirculating solids reactor system, comprises, in general, an oxygen abstraction/adsorption step and a oxygen recovery step or a hydrocarbon and/or an oxygen-containing hydrocarbon partial oxidation step. Although certain reactor systems are preferable to others for practice of the process of the invention, the particular system in which the process is carried out is a matter of choice. The configuration of the system forms no part of the invention. The oxygen adsorption step and the oxygen recovery step or hydrocarbon partial oxidation step of the process can be carried out in a fixed bed system, as illustrated in FIG. 1 , or a moving bed system, as shown in FIG. 2 .

[0036] When the process of the invention is carried out in a fixed bed system, it is preferably carried out as a two-step cyclical process comprising a high temperature oxygen abstraction/adsorption step and an oxygen recovery step or partial oxidation reaction step using the adsorbed oxygen as the oxidant. Suitable fixed bed systems include those comprising a single adsorption/reaction unit, those comprising a battery of adsorption/reaction units operated in phase and those comprising a plurality of adsorption/reactor units or batteries of adsorption/reaction units operated out of phase, whichever is desired. When a system comprising a single unit or a battery of units all of which are operated in phase is used, the adsorption and partial oxidation steps are necessarily intermittent, whereas when a plurality of units are employed in parallel and operated out of phase, one or more units can be in oxygen adsorption service while the partial oxidation reaction is being carried out in one or more other units. In preferred embodiments of the invention, adsorption/partial oxidation cycles are repeatedly carried out in a manner such that production of the desired partial oxidation products is substantially continuous.

[0037] Typical moving bed systems useful for practice of the process of the invention include interconnected multi-vessel systems including an oxygen abstraction/adsorption vessel and a partial oxidation reactor. In a preferred moving bed embodiment, the system is a fluidized bed system, and the partial oxidation reactor may include one or more of a riser section, a fluidized bed section and a moving bed section. Commonly, the reactor comprises both a riser section and a fluidized bed section. Similarly, the unit in which the oxygen adsorption step is carried out may comprise a riser section, a fluidized bed section, a moving bed section or combinations of these. Suitable recirculating bed designs and their operation are described in U.S. Pat. Nos. 4,668,802, 5,021,588 and 5,519,149, the disclosures of which are incorporated herein by reference.

[0038] The process of the invention can be used to produce oxygen from gases such as steam, carbon dioxide, sulfur oxides, nitrogen oxides. The feed gas from which the oxygen is produced can be, for example, an exhaust gas from a combustion process in which a fuel, such as coal, coke or petroleum derivatives, is burned. In one embodiment, the process of the invention is useful for carrying out partial oxidation processes that produce hydrogen and/or carbon monoxide, and perhaps additional partial oxidation products, using substantially pure oxygen that is abstracted and adsorbed by an oxygen ion conducting ceramic from steam and/or carbon dioxide. The oxygen adsorption step is carried out at high temperatures; accordingly, in this embodiment, the at least partially oxygen-saturated mixed conductor leaving the adsorption step is at or near the preferred reaction temperature for the partial oxidation step. In another embodiment, the process can be used to remove harmful components such as sulfur oxides and nitrogen oxides from gas streams, such as waste gases from combustion processes.

[0039] The term “oxygen ion-conducting ceramic” is used herein to define the class of ceramic materials which have an oxygen ionic conductivity of at least 10 ⁻⁵ S/cm (Siemens per centimeter).

[0040] Oxygen ion-conducting ceramics include ceramic materials selected from: (1) perovskite-type ceramics having the structural formula A _1-x M _x BO _3-δ , where A is at least one ion of a metal of Groups 3a and 3b of the periodic table of elements, and it is preferably an f block lanthanide, i.e., rare earth elements, and it is more preferably La, Y, Sm or mixtures of these; M is at least one ion of a metal of Groups 1a and 2a of the periodic table, and it is preferably a Group 2a metal, and it is more preferably Sr, Ca, Ba or mixtures of these; B is at least one ion of a d-block transition metal of the periodic table, and it is preferably Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn or mixtures of these, and it is more preferably V, Fe, Co, Ni, Cu or mixtures of these; x varies from >0 to 1; and δ is the deviation from stoichiometric composition resulting from the substitution of the ions of metal(s) of M for the ions of metal(s) of A; (2) ceramic materials selected from compounds such as Bi ₂ O ₃ , ZrO ₂ , CeO ₂ , ThO ₂ , HfO ₂ and mixtures of these, wherein the ceramic material is doped with CaO, rare earth metal oxides, such as, for example, Y ₂ O ₃ , Nb ₂ O ₃ , Sm ₂ O ₃ , Gd ₂ , O ₃ and mixtures of these; brownmillerite oxides; and mixtures of any of these.

[0041] In preferred embodiments, the adsorbent is an oxygen-selective mixed conductor, which, for purposes of this invention, is defined as a ceramic material which exhibits oxygen ion conductivity of at least 10 ⁻⁵ S/cm and electronic conductivity of at least 10 ⁻⁵ S/cm and whose oxygen ion conductivity and electronic conductivity do not differ from each other by more than two orders of magnitude. Properties of oxygen-selective mixed conductors are set forth in Lin et al., “Oxygen Permeation Through Thin Mixed Conducting Solid Oxide Membranes”, AlChE Journal, May 1994, Vol. 40, No. 5, pp. 786-798, the text of which is incorporated herein by reference.

[0042] Most preferred oxygen-selective mixed conductors are those having the perovskite structure. In perovskite-type mixed conductors, the maximum oxygen adsorbing capability is attained when x of the perovskite structure has a value of 1. Although oxygen adsorption can occur when the value of x in the perovskite-type ceramic used in the process is 0, it is generally not commercially feasible to use perovskite-type ceramics having a value of x less than about 0.01 in the process of the invention. Preferably x has a value of about 0.1 to 1, and most preferably it has a value of about 0.2 to 1.

[0043] When the ceramic material is perovskite-type ceramic, the most preferred rare earth ions in the perovskite-type ceramic are La and Y; M is most preferably Sr and Ca; and B is most preferably Ni, Fe or Cu or mixtures of these.

[0044] Typical of perovskite-type ceramics suitable for use in the invention are La _1-x Sr _x BO _3-δ , Y _1-x Sr _x BO _3-δ , Y _1-x Ca _x BO _3-δ and combinations of these, wherein B is Ni, Fe, Cu or mixtures thereof. Specific useful perovskite-type ceramics are those having the structural formulas: La _0.8 Sr _0.2 Ni _0.8 Fe _0.2 O _3-δ , La _0.7 Ca _0.3 FeO _3-δ , La _0.8 Sr _0.2 MnO _3-δ , La _0.7 Ca _0.3 FeO _3-δ , Y _0.9 Sr _0.1 CrO _3-δ , SrCoO ₃ , etc. In the last compound, SrCoO ₃ , x has a value of 1.

[0045] The oxygen ion conducting ceramic is preferably in particulate form, e.g., it can be powdered, granular, in pellet or bead form or other form which is suitable for use in fixed and/or moving bed processes. It may be in the form of substantially pure mixed conductor, or it may be agglomerated with any suitable binder material, i.e., any material which will not interfere with the performance of the mixed conductor or otherwise adversely affect the safety or performance of the system in which the mixed conductor is used.

[0046] The oxygen ion conducting ceramic may be treated with one or more substances which promote the oxygen abstraction and adsorption properties of the mixed conductor and/or the desired hydrocarbon partial oxidation and/or reforming reactions of the invention and/or other partial oxidation reactions. Suitable promoters include metals of high electric conductivity, such as the transition metals, particularly metals of Groups 1b and 8 of the periodic table of elements. Preferred promoters are Cu, Ag, Fe, Ni, Rh, Pt and mixtures of these. The promoter can be deposited onto the oxygen ion-conducting ceramic in the form of a coating or it can be combined with the ceramic in any other desired form. The particular promoter(s) applied to the ceramic and the method of combining them with the ceramic are not critical and form no part of the invention. For ease of discussion, the oxygen-ion conducting ceramic, with or without the oxygen adsorption and/or partial oxidation reaction promoter(s) and/or other additives, is sometimes simply referred to herein as the mixed conductor. The minimum temperature at which the oxygen adsorption step of the process of the invention is carried out is generally at least about 300° C. This step is preferably carried out at temperatures of at least about 500° C., and is most preferably carried out at temperatures of at least about 650° C. The upper temperature limit for carrying out the oxygen adsorption step is below the temperature at which the oxygen-selective adsorbent begins to melt. Generally the maximum upper temperature is not in excess of about 1,400° C. Preferably, the oxygen adsorption step is carried out at temperatures not exceeding about 1,200° C., and this step is most preferably carried out at temperatures not in excess of about 1,100° C.

[0047] In the organic compound partial oxidation embodiment, the partial oxidation step is generally carried out at or near the temperature at which the adsorption step is carried out. It is often desirable to control the temperature at which the partial oxidation reaction is carried out, to minimize production of carbon dioxide and formation of carbon deposits on the mixed conductor. One method of controlling the partial oxidation temperature is by use of heat exchange means, which, for example, may be in the form of tubing, preferably positioned in the upper section of the reactor.

[0048] Another, and often preferred method of controlling the temperature in the reactor is to introduce a moderating agent, such as steam or carbon dioxide, into the reactor. This provides the additional benefit of reforming the hydrocarbon reactant to produce additional hydrogen and/or carbon monoxide. The moderating agent can be introduced into the reactor at various points, as described below in more detail.

[0049] The pressure at which the adsorption step of the process is carried out is a matter of choice and, in general, is not critical. Typically, this step is carried out at a pressure at or above about 1 bar, absolute (bara). The minimum pressure at which the adsorption step is carried out is preferably about 0.5 bara and is most preferably about 5 bara. The upper pressure limit of the adsorption step of the process is determined by economics and limitations of the reaction system and, in general, this step is desirably carried out at absolute pressures not in excess of about 50 bara, is preferably carried out at pressures not in excess of about 20 bara, and is most preferably carried out at pressures not in excess of about 15 bara.

[0050] The pressure at which the partial oxidation step is carried out is likewise a matter of choice and not critical. In general, the adsorption step and the partial oxidation step are usually carried out at substantially the same pressure.

[0051] In the organic compound partial oxidation embodiment, the particular organic compound used as feed in the partial oxidation step of the process of the invention is a matter of choice. The organic compound is usually a hydrocarbon, or an oxygen-containing compound. For ease of discussion, this reactant will generally be referred to hereinafter simply as “hydrocarbon”. The hydrocarbon may be any aliphatic, cycloaliphatic or aromatic hydrocarbon having 1 to 12 or more carbon atoms, and it may be saturated or ethylenically unsaturated and straight chain or branched chain. In preferred embodiments of the invention, the hydrocarbon is in the gaseous state under the conditions at which the partial oxidation reaction takes place. Oxygen-containing hydrocarbons which may be used as feed for the partial oxidation reaction include alcohols, ethers, aldehydes, ketones, carboxylic acids, etc. Preferred aliphatic hydrocarbons include those having 1 to 6 carbon atoms, and preferred aromatic hydrocarbons include those having up to twelve carbon atoms. More preferred hydrocarbons are those having 1 to 4 carbon atoms. Typical hydrocarbons include methane, methanol, ethane, propane, the butanes, benzene, the xylenes, refined petroleum fractions, such as naphtha and gasoline, methanol, ethanol, etc. Preferred hydrocarbon feeds include methane, methanol, ethane, ethene, propane, propene, n-butane, i-butane, n-butylene, l-butylene, butadiene, the pentanes, pentenes, hexanes and hexenes,. Most preferred hydrocarbon feeds for the production of hydrogen and carbon monoxide by the process of the invention are methane, methanol and natural gas.

[0052] Since oxygen-containing gases other than air or mixtures of oxygen and other gases are used as the source of oxygen for the hydrocarbon partial oxidation processes, there is no danger of forming an explosion hazard at any point in the process. Accordingly, there is no need to include a stripping step between the partial oxidation step and the oxygen abstraction/adsorption step to remove residual unreacted hydrocarbon and/or partial oxidation reaction product from the mixed conductor. However, a post-partial oxidation stripping step can be included in the process, if desired. This can be accomplished, for example, by stripping the spent adsorbent with a gaseous substance that is compatible with the partial oxidation product gas. By “compatible” is meant that the gaseous substance can be used in the process of the invention without creating undue safety hazards, and it is easily separable from the product gas or its presence in the product gas is not objectionable with respect to the intended use or further processing of the product gas. Suitable stripping gases include steam and carbon dioxide.

[0053] It may also be desirable to include an evacuation step in place of or in addition to the stripping step to more completely recover any product gas remaining in the mixed conductor after the partial oxidation step. The evacuation step can be carried out to any desired pressure. For example, the pressure can be reduced to about 0.1 bara or lower, but, for economic purposes, it is preferably not reduced to below about 0.2 bara at this stage of the process.

[0054] As mentioned above, a reaction moderating agent, such as steam or carbon dioxide or both of these can be passed through the reaction zone in addition to the hydrocarbon during the second step of the process. This is desirable when the quantity of oxygen present in the mixed conductor is insufficient to convert all of the hydrocarbon to the desired partial oxidation products and/or when coking of the mixed conductor occurs in the reactor. The advantage of this variation is that reforming of the hydrocarbon and/or conversion of carbon deposits on the mixed conductor to carbon monoxide occurs in addition to partial oxidation of the hydrocarbon.

[0055] Steam and carbon dioxide used as moderating agents react with unreacted hydrocarbon and carbon deposits on the mixed conductor to produce additional hydrogen and/or carbon monoxide by, for example, one or more of the following reactions, when the hydrocarbon is methane:

CH ₄ +H ₂ O→CO+3H ₂

CH ₄ +CO ₂ →2CO+2H ₂

C+H ₂ O→CO+H ₂

C+CO ₂ →2CO

[0056] The moderating agent can be introduced into the partial oxidation reactor with or separately from the hydrocarbon. In fluidized bed embodiments, the at least partially oxygen-saturated mixed conductor can be fluidized and carried into the partial oxidation reactor by the gaseous hydrocarbon reactant and/or by the steam and/or carbon dioxide. The steam and/or carbon dioxide reforming reaction can take place even after substantially all of the sorbed oxygen is consumed by the partial oxidation reaction. Since the reforming reaction is endothermic, it may be desirable or necessary in some cases to provide supplemental heat to the reaction zone to compensate for heat consumed in the reforming reaction. Supplemental heat can be provided by any suitable means, such as by the use of heaters.

[0057] If desired, the partial oxidation step of the process can be used to produce partial oxidation products in addition to carbon monoxide and hydrogen. This can be accomplished by combining a catalyst which promotes the desired additional partial oxidation reaction with the oxygen ion conducting ceramic and using the appropriate hydrocarbon as the feed stream.

[0058] The invention can be more easily understood by reference to the appended drawings, considered in conjunction with the following description. Equipment that is not necessary for an understanding of the invention, such as auxiliary valves, storage vessels and pumps, have not been included in the illustrated system.

[0059] Turning now to the drawings, and particularly to FIG. 1 , illustrated therein is a two vessel partial oxidation system comprising reaction vessels A and B, arranged in parallel. Vessels A and B are packed with a particulate adsorbent of the type described above, for example a perovskite ceramic material. At the inlet end, the system is provided with steam/carbon dioxide feed line 2 , which is connected to manifold 4 . Manifold 4 can be put into fluid communication with reaction vessel feed lines 10 and 12 via valves 6 and 8 , respectively. Lines 10 and 12 are connected to the inlet ends of reaction vessels A and B, respectively. The inlet end of the system is also provided with hydrocarbon feed line 14 , which is attached to manifold 16 at a point between valves 18 and 20 , also provided in manifold 16 . Manifold 16 can be put into fluid communication with lines 10 and 12 via valves 18 and 20 , respectively.

[0060] On their outlet ends, vessels A and B are connected to lines 22 and 24 , respectively. Lines 22 and 24 are connected to manifold 26 , and flow control to manifold 26 from lines 22 and 24 is provided by valves 28 and 30 , which are attached to manifold 26 . Also attached to manifold 26 , at a point between valves 28 and 30 , is hydrogen/carbon monoxide discharge line 32 . Lines 22 and 24 are also joined to manifold 34 . Lines 22 and 24 can be put into fluid communication with manifold 34 through valves 36 and 38 , respectively. Manifold 34 is connected to partial oxidation reaction product gas line 50 at a point between valves 36 and 38 .

[0061] The system illustrated in the drawing is designed to be operated in semi-continuous fashion, with reactors A and B being operated 180° out of phase, so that reactor A is in oxygen adsorption-hydrogen/carbon monoxide production service while reactor B is in partial oxidation reaction service, and vice versa. The process of the invention, as carried out in the system illustrated in FIG. 1 , will be described in detail as a two-stage hydrocarbon partial oxidation process comprising a first stage, in which reactor A is in oxygen adsorption-hydrogen/carbon monoxide production mode and reactor B is in partial oxidation reaction mode, and a second stage, in which reactor B is in oxygen adsorption-hydrogen/carbon monoxide production mode and reactor A is in partial oxidation mode.

[0062] At the beginning of the first stage, valves 6 , 20 , 28 and 38 are open and all other valves are closed. Steam or carbon dioxide, introduced into the system through line 2 , passes through line 10 and enters vessel A. While the adsorption-hydrogen/carbon monoxide production stage of the process is being carried out in vessel A, the oxygen ion conducting ceramic in vessel A is maintained at a temperature in the range of about 500 to about 1400° C.

[0063] Since the overall process is endothermic, it is usually necessary to apply heat to the system to maintain the adsorbent at the desired temperature. Heat can be provided in a variety of ways. For example, heat can be provided to the system by direct or indirect heating techniques. A preferred direct heating procedure is to combust a fuel, such as coal, coke, fuel oil or other hydrocarbon-based fuels, etc., and introduce the hot exhaust gas from the combustion process directly into the chamber in which the abstraction/adsorption process is carried out. This procedure has the dual advantage of providing heat and supplying the feed gas for the oxygen abstraction step. The combustion process is preferably carried out in the full combustion mode to maximize production of carbon dioxide and steam. Other oxygen-containing gases, such as sulfur and nitrogen oxides may also be present in the hot exhaust gas. As noted above, oxygen can also be abstracted from these components. Another method of providing heat to the reaction zone is to introduce supplemental oxygen into the reaction zone during the oxygen adsorption step or during the hydrocarbon partial oxidation step or between these steps. Adsorption of the oxygen provides heat in the adsorption step and additional combustion of the hydrocarbon with supplemental oxygen provides heat in the second step of the process. Other heating techniques that can be used in the process include internal and external indirect heaters, such as electric and/or fuel-fired heaters whose coils pass through the bed of mixed conductor. Heat can also be applied by using heated feeds, such as superheated steam. Another useful heating procedure is to incorporate the reaction zone in a furnace zone. The method used to provide heat to the reaction zone is a matter choice and forms no part of this invention.

[0064] Distribution of heat in the reaction zone can, if desired, be facilitated by incorporating a material having a high thermal conductivity into the reaction zone. As mentioned above, this can be accomplished by mixing or sandwiching, i.e. layering, the mixed conductor with a high temperature stable material, such as a heat conducting ceramic material or a particulate metal material. Heat distribution in the reaction zones can also be assisted by strips or rods of metallic material inserted in, upstream of or downstream of the reaction zones. If it is desirable or necessary to remove heat from the reaction zone to prevent excessive heating of the mixed conductor contained therein, this can be accomplished by means of the above-described heat transmission means.

[0065] In any event, the steam and/or carbon dioxide feedstream entering vessel A passes upwardly through the oxygen ion conducting ceramic contained therein, and as it does so, oxygen is abstracted from the steam and/or carbon dioxide by the mixed conductor and hydrogen and/or carbon monoxide are produced. The hydrogen and/or carbon monoxide leaves vessel A through line 22 and passes out of the system through manifold 26 and line 32 and is sent to storage or further processing or to a downstream application. As the adsorption step proceeds in vessel A, the adsorbed oxygen forms a front which advances through the bed of mixed conductor toward the nonadsorbed product outlet end of vessel A.

[0066] While the oxygen abstraction step is taking place in vessel A the partial oxidation step is initiated and carried on in vessel B. During this stage of the cycle, hydrocarbon feed is introduced into vessel B through lines 14 and 12 . If desired, the hydrocarbon feed may be compressed to the desired pressure by any suitable means, such as by a compressor or gas blower, or the gas may be provided from its source as a pressurized gas stream. As the hydrocarbon gas contacts the at least partially oxygen-saturated mixed conductor in vessel B, it reacts with the oxygen sorbed onto the mixed conductor to produce the desired partial oxidation gas product, which is generally a mixture of hydrogen and carbon monoxide. The product gas stream may also contain other gaseous by-products, such as carbon dioxide and moisture, but the concentration of these by-products can be minimized by maintaining optimum reaction conditions in the reaction vessel. The hot reaction gases pass out of vessel B through lines 24 and 40 and they pass, for example, to storage together with or separately from the hydrogen and/or carbon monoxide being discharged from vessel A, or they can be sent to downstream processing units. As the partial oxidation reaction progresses in vessel B, the mixed conductor in this vessel is regenerated by at least partial depletion of the sorbed oxygen therefrom.

[0067] At a predetermined point in the first stage of the process, such as when the adsorbed oxygen front reaches a desired point in vessel A, or when all of the oxygen in vessel B is reacted with hydrocarbon, the first stage of the cycle is terminated and the second stage begins. By proper sizing of the reaction vessels and careful control of the reactant gas flow rates, etc., the process can be designed so that the adsorption step in vessel A reaches its desired end point at substantially the same time that all of the sorbed oxygen in vessel B is reacted. Alternatively, if the adsorption step in vessel A reaches its desired end point before the oxygen in vessel B is completely reacted, or vice versa, the completed part of the first stage of the process can be terminated and further activity in that vessel can be suspended until the other part of the first stage reaches its desired end point.

[0068] Upon completion of the first stage of the process, the second stage is begun. During the second stage valves 8 , 18 , 30 and 36 are open and all other valves are closed. Steam and/or carbon dioxide, introduced into the system through line 2 , now passes through line 12 and enters vessel B. As the steam and/or carbon dioxide passes through vessel B, oxygen is adsorbed by the regenerated mixed conductor in this vessel. Hydrogen and/or carbon monoxide now passes out of vessel B through line 24 and leaves the system through line 32 . Meanwhile, the partial oxidation step is initiated and carried on in vessel A. During this stage of the cycle, hydrocarbon is introduced into vessel A through lines 14 and 10 . As the hydrocarbon contacts the hot mixed conductor in vessel A, it reacts with the oxygen sorbed onto the mixed conductor to produce the desired partial oxidation gas product The hot reaction gases pass out of vessel A through line 22 and passes out of the system through line 40 .

[0069] When the desired stage 2 end point is reached, the second stage of the process (and the current cycle) ends and the next cycle begins with vessel A in oxygen adsorption-hydrogen/carbon monoxide production mode and vessel B in partial oxidation reaction mode.

[0070] As mentioned above, it may sometimes be desired to reform unreacted hydrocarbon or partially oxidize carbon deposits on the mixed conductor in the vessel in which the partial oxidation reaction is being carried out,. Reforming can be carried out by introducing steam or carbon dioxide as moderating agent into the vessel undergoing the partial oxidation reaction together with the hydrocarbon being fed to this vessel. This can be accomplished, for example, by opening valve 6 , while the partial oxidation is being carried out in vessel A, or valve 8 , while the partial oxidation is being carried out in vessel B.

[0071] Since, as noted above, these reactions are endothermic, additional heating of the reactants may be required. Although most or all of the additional heat required for the reactions can be provided by the hydrocarbon partial oxidation reaction, supplemental heating can be provided, if necessary, by other heating means (not shown).

[0072] FIG. 2 illustrates a system for practice of the process of the invention by the fluidized bed technique. The system of FIG. 2 includes, as principal units, oxygen abstractor/adsorber A, partial oxidation reactor R, and optional steam stripper S. Vessel A, as noted above, can be any type of equipment which provides intimate contact between a particulate material and a gas. In the system illustrated in FIG. 2 , vessel A includes dense phase section 102 , positioned at the lower end of the vessel, and dilute phase section 104 , located above dense phase section 102 . Vessel A is also provided with steam/carbon dioxide inlet line 106 , hydrogen/carbon monoxide outlet line 108 , oxygen-depleted mixed conductor return line 110 and oxygen-containing mixed conductor line 112 . Line 112 is connected to the lower part of hydrocarbon feed inlet line 114 , which, in turn, is connected to the lower part of partial oxidation reactor R.

[0073] Reactor R can be any type of reactor suitable for carrying out moving catalyst bed partial oxidation reactions. In the system illustrated in the drawing, reactor R includes riser section 116 and dilute phase section 118 , positioned above riser section 116 . In embodiments of the invention in which hydrocarbon reforming is practiced as part of the process, it may be carried out in part of, for example in the upper portion of, section 118 . In such embodiments, reactor R can be provided with moderating gas inlet line 120 , the upstream end of which is connected to moderating gas supply line 122 . Section 118 is also provided with oxygen-depleted mixed conductor discharge line 124 and product gas discharge line 126 . The downstream end of line 124 is connected to oxygen-depleted mixed conductor stripper S.

[0074] When stripper S is included in the system, it can be any vessel suitable for stripping a particulate material with a stripping gas. Stripper S is provided with stripping gas inlet line 128 , the upstream end of which, in the embodiment illustrated in FIG. 2 , is connected to moderating gas supply line 122 , and stripping gas outlet line 130 , The upstream end of oxygen-depleted mixed conductor line 110 is connected to stripper S.

[0075] In practicing the process of the invention in the system illustrated in FIG. 2 , particulate mixed conductor of the type described above is circulated in fluidized form through the system comprising abstractor/adsorber A, reactor R and stripper S. In vessel A, recycled mixed conductor is contacted with steam and/or carbon dioxide at a temperature and pressure in the ranges specified above. The steam and/or carbon dioxide enters vessel A through line 106 and passes upwardly through this vessel. The desired adsorption temperature can be initially established in vessel A by any suitable means, such as by superheating the steam or heating the carbon dioxide entering this vessel or by internal or external heating means, as described above in the description of the FIG. 1 system. The method used to heat the steam and/or carbon dioxide and/or the mixed conductor in vessel A during, for example, start-up is a matter of choice and forms no part of this invention.

[0076] The steam and/or carbon dioxide entering vessel A passes upwardly through dense phase zone 102 , and as it does so, it comes into intimate contact with mixed conductor that is descending through zone 102 . As indicated above, the counterflow arrangement illustrated in the drawing is only one of several methods of steam/carbon dioxide-mixed conductor contact that can be employed. As the steam and/or carbon dioxide contacts the mixed conductor, oxygen abstracted from the steam and/or carbon dioxide is adsorbed by the mixed conductor, thereby at least partially saturating the mixed conductor with oxygen. The hydrogen and/or carbon monoxide produced during the oxygen abstraction rises into dilute phase zone 104 where it separates from the particulate mixed conductor. One or more cyclone separators can be positioned in the upper part of section 104 to facilitate separation of the hydrogen and/or carbon monoxide from the mixed conductor. The hydrogen and/or carbon monoxide exits vessel A through line 108 , and is sent to storage or to downstream processing.

[0077] The hot, at least partially oxygen saturated mixed conductor passes through line 112 and enters line 114 . The mixed conductor mixes with gaseous hydrocarbon feed, for example, methane, entering reactor R through line 114 , and the mixture flows upwardly through riser section 116 of reactor R. As the hot mixed conductor and hydrocarbon mix, the hydrocarbon undergoes partial oxidation, producing a gas mixture comprised substantially of carbon monoxide and hydrogen, according to the following equation, in which the hydrocarbon is methane:

2CH ₄ ( g )+O ₂ ( s )→2CO( g )+4H ₂ ( g )

[0078] The temperature and rate of mixed conductor and hydrocarbon flow through reactor R are preferably maintained at levels that maximize production of hydrogen and/or carbon monoxide and minimize the formation of carbon dioxide and coking of the mixed conductor. After passing through riser 116 of reactor R, the mixed conductor-gas mixture enters dilute phase section 118 , where the velocity of the mixture decreases sufficiently to effect separation of the mixed conductor and gas phase. As was the case in vessel A, separation of the mixed conductor and product gas can be assisted by means of gas separators, such as cyclone separators situated at the top of fluid section R. The product gas passes out of reactor R through line 126 and is sent to storage or to a downstream application. If desired, the product gas stream can be sent to adsorption or other gas separation means to recover unreacted hydrocarbon therefrom. The recovered hydrocarbon can be recycled to reactor R, if desired.

[0079] The at least partially oxygen-depleted mixed conductor separated from the gas product leaves reactor R through line 124 and may return directly to vessel A or it may enter stripper S. In the latter case, the spent mixed conductor passes through stripper S, where entrained product gas is stripped therefrom by steam or carbon dioxide or other appropriate stripping gas, introduced into stripper S through line 128 . The stripped gas-stripping agent mixture passes out of stripper S through line 130 , and is sent to storage or otherwise processed or disposed of.

[0080] The clean mixed conductor is recycled to vessel A through line 110 . Fresh mixed conductor can be introduced into the system at any desired point, for example by adding it to vessel A through fresh mixed conductor filling means (not shown).

[0081] It will be appreciated that it is within the scope of the present invention to utilize conventional equipment to monitor and automatically regulate the flow of gases within the system so that it can be fully automated to run continuously in an efficient manner.

[0082] The invention is further illustrated by the following examples in which, unless otherwise indicated, parts, percentages and ratios are on a volume basis. Gas flow rates are at standard temperature and pressure. Example 1 is based on experimental results and Example 2 is hypothetical.

EXAMPLE 1

[0083] This experiment was carried out in a fixed-bed reactor similar to the system illustrated in FIG. 1 , except that a single reactor was used. The reactor, which has an inner diameter of 1.6 inches and a length of 24 inches, was packed with about 200 g of La _0.8 Sr _0.2 Ni _0.8 Fe _0.2 O _3-δ perovskite-type ceramic material, coated with 5 wt % Ni. The ceramic material was in the form of a monolithic structure. Operation of the reactor system was controlled by a PLC programming controlling system and a computer, and feed flow rates and the reactor temperature were controlled by mass flow controllers and temperature controllers.

[0084] The experiment was carried out in two steps, an oxygen abstraction/adsorption step and a methane partial oxidation step. During the oxygen abstraction/adsorption step, which lasted about 6.8 minutes, a steam-nitrogen mixture containing 80% nitrogen was introduced into the reactor at a flow rate of 1.5 l/min (liters per minute, dry basis). During the methane partial oxidation step, which lasted about 1 minute, a methane-steam mixture containing 20% steam was introduced into the reactor at a flow rate of 2 l/min. The reactor temperature was maintained at 800° C. by means of an electric furnace. The pressure in the reactor was maintained at about 8 psig. The effluent gas composition was instantaneously measured by a gas analyzer. During the oxygen abstraction/adsorption step, product gas having an average composition of 15.5% H ₂ and 84.5% N ₂ (on a dry basis) exited the reactor at an average flow rate of about 1.4 l/min. During the methane partial oxidation step, product gas having an average composition of 68.4% H ₂ , 27.5% CO and 4.16% CO ₂ (on a dry basis) exited the reactor at an average flow rate of 4.9 l/min. Steam conversion during the oxygen abstraction/adsorption step was about 74% while steam and methane conversions during the methane partial oxidation step were respectively 62% and 97%.

EXAMPLE 2

[0085] This example is simulated using a circulating reactor similar to the system illustrated in FIG. 2 , but without an adsorbent stripping zone. The oxygen selective mixed conductor is assumed to be a particulate perovskite ceramic of the formula La _0.8 Sr _0.2 Ni _0.8 Fe _0.2 O _3-δ (coated with 5 wt % Ni) having a particle size of about 20 to 100 microns. The oxygen abstraction/adsorption and partial oxidation reaction zones are each assumed to be maintained at a temperature of about 850° C. The selected pressure in the adsorption zone is about 20 psig, and the pressure in the reaction zone is lower than the pressure in the adsorption zone. Simulated steam feed to the adsorption zone of the system is 13.93 l/min and simulated methane feed to the reactor zone is 10 l/min. The selected solids residence time in the adsorption zone is in the range of 10 sec. to 10 min., and that in the reaction zone is in the range of 20 sec. to 20 min. The selected gas residence time in the adsorption zone is in the range of 0.001 to 10 sec., and that in the reaction zone is in the range of 0.01 to 100 sec.

[0086] Based on these conditions, a product stream at a flow rate of about 28.5 l/min and containing 65.5% hydrogen, 29.5% carbon monoxide, 1.72% methane, 3.28% carbon dioxide (on a dry basis) is projected to be produced. The exhaust gas from the adsorption zone is projected to be 10.45 l/min and it is projected to be almost pure hydrogen (on a dry basis). Methane and steam conversions are selected respectively to be 95% and 75%. Hydrogen selectivity is projected to be 100%, and carbon monoxide selectivity is selected to be 90%.

EXAMPLE 3

[0087] This experiment was carried out in the reactor system described in Example 1, except that 50 g of La _0.8 Sr _0.2 Co _0.5 Fe _0.5 O _3-δ perovskite-type ceramic material was used as the mixed conductor. The experiment was carried out in two steps, an oxygen abstraction/adsorption step and a methane partial oxidation step. During the oxygen abstraction/adsorption step, which lasted about 3 minutes, CO ₂ was introduced into the reactor at a flow rate of 1.0 l/min (liters per minute). During the methane partial oxidation step, which lasted about 2 minutes, a methane-steam mixture was introduced into the reactor at a flow rate of 1.0 l/min. The reactor temperature was maintained at 1000° C. by means of an electric furnace. The pressure in the reactor was maintained at about 9 psig. The effluent gas composition was instantaneously measured by a gas analyzer. During the oxygen abstraction/adsorption step, product gas having an average composition of 18.9% CO ₂ and 81.1% CO exited the reactor at an average flow rate of about 1.26 l/min. During the methane partial oxidation step, product gas having an average composition of 71.5% H ₂ , 25.6% CO, 0.7% CO ₂ and 2.2% CH ₄ (on a dry basis) exited the reactor at an average flow rate of 2.58 l/min. CO ₂ conversion during the oxygen extraction/adsorption step was about 76% while methane conversion during the methane partial oxidation step was 94.2%.

[0088] These examples illustrate steam/carbon dioxide decomposition to oxygen and hydrogen/carbon monoxide, and partial oxidation of methane to hydrogen and carbon monoxide in both fixed-bed and fluidized bed reactors using particulate perovskite-type ceramic material as the oxygen adsorbent.

[0089] Although the invention has been described with particular reference to a specific equipment arrangement and to specific examples, these features are merely exemplary of the invention and variations are contemplated. For instance, the invention can be practiced by conducting the hydrocarbon partial oxidation step in the liquid phase. Furthermore, as stated above, the process of the invention can be carried out in systems which are variations of the systems illustrated in the drawings. The scope of the invention is limited only by the breadth of the appended claims.